Product Profile
Hardener 2251 is designed for epoxy resin and it is for heating operation under low temperature.
Technical indicator
|
Technical index |
Data |
|
Viscosity (25℃) |
50-100 |
|
Proportion (25℃) |
0.95 |
|
Amine value (mgKOH/g) |
300 |
|
Active hydrogen equivalent |
87 |
|
Gelation time (25℃/100g)minutes |
75 |
|
Film hardening time (25℃) hours |
6 |
|
Complete hardening time (70/25℃) hours |
18 |
Advantage
■ Low viscosity
■ High glossy
■ Long operation time
■ High mechanical strength
Mechanical property
| Mechanical property | Curing process | |
| Tensile strength | 60.5Mpa | 8hours fully cured at 50-60℃ |
| Bending strength | 96.6Mpa | 5hours fully cured at 70-80℃ |
| Bending failure load | 272N | |
| Tensile failure load | 2702N | |
Product Application
Epoxy floor artesian plane coating/casting material
FRP water softening tank production(winding technology)
Product detail pictures:
Related Product Guide:
Fast and superior quotations, informed advisers to help you choose the correct merchandise that suits all your requirements, a short generation time, responsible quality control and different services for paying and shipping affairs for Low MOQ for Epoxy Resin For Frp Water Tank - Hardener 2251 – Huabin, The product will supply to all over the world, such as: Hungary, moldova, Cyprus, We have more than 8 years of experience in this industry and have a good reputation in this field. Our products have won praise from customers worldwide. Our aim is to help customers realize their goals. We are making great efforts to achieve this win-win situation and sincerely welcome you to join us.
By Nicci Hackner from Zimbabwe - 2017.10.25 15:53
The factory workers have rich industry knowledge and operational experience, we learned a lot in working with them,we are extremely grateful that we can encount a good company has excellent wokers.
By Beulah from Italy - 2017.03.07 13:42