High Performance Epoxy Resins For Electrical Insulation - Hardener 2251 – Huabin
High Performance Epoxy Resins For Electrical Insulation - Hardener 2251 – Huabin Detail:
Product Profile
Hardener 2251 is designed for epoxy resin and it is for heating operation under low temperature.
Technical indicator
|
Technical index |
Data |
|
Viscosity (25℃) |
50-100 |
|
Proportion (25℃) |
0.95 |
|
Amine value (mgKOH/g) |
300 |
|
Active hydrogen equivalent |
87 |
|
Gelation time (25℃/100g)minutes |
75 |
|
Film hardening time (25℃) hours |
6 |
|
Complete hardening time (70/25℃) hours |
18 |
Advantage
■ Low viscosity
■ High glossy
■ Long operation time
■ High mechanical strength
Mechanical property
| Mechanical property | Curing process | |
| Tensile strength | 60.5Mpa | 8hours fully cured at 50-60℃ |
| Bending strength | 96.6Mpa | 5hours fully cured at 70-80℃ |
| Bending failure load | 272N | |
| Tensile failure load | 2702N | |
Product Application
Epoxy floor artesian plane coating/casting material
FRP water softening tank production(winding technology)
Product detail pictures:
Related Product Guide:
We have been committed to offering easy,time-saving and money-saving one-stop purchasing service of consumer for High Performance Epoxy Resins For Electrical Insulation - Hardener 2251 – Huabin, The product will supply to all over the world, such as: Georgia, India, Borussia Dortmund, We have been very responsible for all details on our customers order no matter on warranty quality, satisfied prices, quick delivery, on time communication, satisfied packing, easy payment terms, best shipment terms, after sales service etc. We provide one-stop service and best reliability to our every customers. We work hard with our customers, colleagues, workers to make a better future.
By Zoe from Turkey - 2017.12.09 14:01
The company keeps to the operation concept "scientific management, high quality and efficiency primacy, customer supreme", we have always maintained business cooperation. Work with you,we feel easy!
By Liz from Spain - 2017.12.09 14:01