Product Profile
Hardener 2251 is designed for epoxy resin and it is for heating operation under low temperature.
Technical indicator
Technical index |
Data |
Viscosity (25℃) |
50-100 |
Proportion (25℃) |
0.95 |
Amine value (mgKOH/g) |
300 |
Active hydrogen equivalent |
87 |
Gelation time (25℃/100g)minutes |
75 |
Film hardening time (25℃) hours |
6 |
Complete hardening time (70/25℃) hours |
18 |
Advantage
■ Low viscosity
■ High glossy
■ Long operation time
■ High mechanical strength
Mechanical property
Mechanical property | Curing process | |
Tensile strength | 60.5Mpa | 8hours fully cured at 50-60℃ |
Bending strength | 96.6Mpa | 5hours fully cured at 70-80℃ |
Bending failure load | 272N | |
Tensile failure load | 2702N |
Product Application
Epoxy floor artesian plane coating/casting material
FRP water softening tank production(winding technology)
Product detail pictures:
Related Product Guide:
To regularly increase the management program by virtue from the rule of "sincerely, good religion and high quality are the base of enterprise development", we greatly absorb the essence of linked products internationally, and constantly produce new goods to satisfy the calls for of shoppers for factory Outlets for Clear Epoxy Resin For Frp Pipe - Hardener 2251 – Huabin, The product will supply to all over the world, such as: Washington, Rio de Janeiro, Comoros, Our factory insists on the principle of "Quality First, Sustainable Development", and takes "Honest Business, Mutual Benefits" as our developable goal. All members sincerely thanks for all old and new customers' support. We will keep working hard and offering you the highest-quality products and service.Thanks.
By Norma from Chicago - 2017.10.23 10:29
Customer service staff and sales man are very patience and they all good at English, product's arrival is also very timely, a good supplier.
By Fanny from Jamaica - 2017.09.30 16:36